CODE: Q 900
Vernici anticorrosive
Via Niccol€ Tommaseo 61 Collegno ( TO ) ITALY
Tel + 39 011 411.17.18 + 39 011 411.17. 21
25.06.2013
Name of product:
DESCRIPTION: VIRPOL Q 900 is an enamel acrylic-polyurethane modified aliphatic resins with two components to finish, with an excellent outdoor resistance, produced with low solvent content, the type "surface tolerant" aliphatic catalyzed with catalyst 44, or with a catalyst for high dry solid
HS 88 aliphatic always.
POL 900 VIR Q, is applied to the epoxy-polyamide primer V86 / epoxy dast to complete several cycles corrosion, where stringent conditions to exposure to the elements, chemicals and does not affect the final coating.
VIR POL Q 900 is a product approved by Istituto Scientifico Breda SpA -Test Report No.
187/BA/AC98093, with excellent result for the value of the spectral energy reflection of solar radiation exposure outside after irradiation with a xenon lamp, with excellent performance over 100 continuous hours.
TECHNICAL CARATTERISTIC
Odor
Color
Surface appearance
Brilliance ISO 2813
Specific weight UNI 8910
Dry residue
Flash point
Theoretical yeld 70-80 micron
Method of application
Rapport of application in weight
Nozzle pressure
Diametre pressure
Operating temperature
Diluent to be used
Diluition caratteristic
FOLDER RAL perfectly relaxed
65 GLOSS+ 2 SEMIGLOSS- 98 gloss for lucid/brilliance
1.360 kg/lt
70%
> 20 • flammable
220 gm/mq brush/airless in weight 3:1 ( 6 kg of part A + 2 kg part B hardener 44 ) in volume 3,5:1 ( 700 ml of part A + 200 ml part B herdener. N44
150 bar/2220 psi
0,17”-0,19” min 15 •c umiditƒ max 80% diluent 622
10%
Essication 15•-20•degrees at touch 8 hours, essication 18-24 hours
Complete catalysis 168 hours
V.O.C 220 gr/lt
Pot life 4 hours
Recommended film thickness
Viscosity of application
40-60 micron
90” tazza Ford 4
Recommended number of hands 1- 2 hands

PREPARATION ON THE SURFACE
The surface must be completely clean and dry at time of application and its: temperature should be less than above the dew point to avoid condensation.
The application with a temperature of 0 • C or lower can determine the formation of surface ice that compromises the adhesion
The presence of high humidity and condensation on the surface to during application and the subsequent 10 hours at 20 • C can influence the formation of the paint film.
In confined spaces provide adequate ventilation during application and drying.
CHEMICAL AND MECHANICAL CARATTERISTIC
Grid UNI ISO 24091
Salt spray UNI ISO 9227
Abrasion resistance UNI 93881
100% no retraction on the gridded surface
> 100 hours only primer excellent
Resistenza agli agenti chimici e acidi excellent
Resistance at UV excellent > 500 hours on spessor > 50 micron
Resistance reflection Energy > 100 hours continuative with lamp xeno
Norma ASTM G 26 Method C
Reflectance value-reflection energy
Conservability
Content excellent a 0 – 20 grad, con 200 cycle per 2,5 mounths
6 mounths in a dry place over 10 •C in latte da 25 kg + 8 kg for semigloss + 12,5 kg for lucid
RECOAT TIMES: Time min. Covering 6 h.
Max no time
Fund v. 86 / dast bottom epoxy finish vir pol + q 900
Applicable also wet on wet, after about 30/40 minutes from the bottom
The data shown are correct at the time of the Quality Control and refer to standardized environmental conditions.
The information on this tab, unable to take account of the specific conditions of each application, are indicative
VIRES s.r.l.
Via Niccol€ Tommaseo 61 Collegno ( TO ) Italy
Tel + 39 011 411.17.18 fax + 39 011 411.17. 21 info@vires.it
www vires.it